Outdoor Epoxy Resin
LE- 9516/LH-9516 Syetem
|
Epoxy resin Hardener Filler Color paste |
LE-9516 LH-9516 Silica LC- |
100pb w 100pbw 350-400pbw 3pbw |
Formulation |
|
A two component saturated epoxy resin system without premixed filler, liquid at room temperature. Performance It is suitable for both APG injection process and vacuum casting process. Excellent UV resistance, excellent thermal and thermal shock resistance, excellent environmental resistance and excellent electromechanical performance. |
|||
|
Outdoor high-voltage electrical insulation parts such as: insulators, transformers and other insulation products. |
Application | ||
Resin LE-9516 is a modified saturated epoxy resin system .
Physical and chemical indicators
Curing agent LH-9516 is a modified weathering anhydride curing agent.
| Property | Unit | Standard | Property | Unit | Standard | |
| Appearance | Visual | Transparent-yellow liquid | Appearance | Visual | Transparent-yellow liquid | |
| Epoxy value | Eq/kg | 4.0-4.5 | viscosity at 25℃ | mPa.s | 150-400 | |
| viscosity at 25℃ | mPa.s | 500- 1500 | Density at 25℃ | g/cm3 | 1.17- 1.24 | |
| Density at 25℃ | g/cm3 | 1.16- 1.20 | VP | Pa | About 0.5 | |
| VP at 25℃ | Pa | <0.01 | Flash point | ℃ | About 140 | |
| Flash point | ℃ | About 135 |
Epoxy resin LE-9516, curing agent LH-9516 and a certain amount of filler can be mixed
according to the following curing process after fully mixing under vacuum conditions:
Process
| Processing parameters | Automatic Pressure Gelation | Vacuum casting |
| Epoxy Resin/Hardener mixing temperature | 40℃/1-2h | 50-60℃/1- 1.5h |
| Feeding method | Pressure(0.5-5bar) | Vacuum (casting pot) |
| Mold temperature | 130-150℃ | 105℃/4-6h |
| Gelation time | 10-50mins | 80℃/4h+100℃/2h+120℃/2h |
| Post-curing | 130-140℃×6-10h | 130-140℃×6-10h |
Page1 of 2 9516 Specification Page1 of 2
LE-9516:LH-9516=100:100
Gel time
| Temperature | Gel time |
| at 120℃ | 20-40mins |
| at 140℃ | 9-18mins |
| at 160℃ | 4-8mins |
Mechanical and physical properties
Test system: Resin LE- 9516 / curing agent LH-9516 / silica flour=100/100/400 Curing conditions: 120 ° C × 4hours +
140 ° C × 8hours
Note: The following performance data are measured according to the national standard and are for user reference only.
The specific application data should be determined according to the actual conditions of the user.
| Properties | Typical results | Properties | Typical results | |
| Tg(DSC) | 60-80℃ | Thermal decomposition temperature | >320℃ | |
| tensile strength | 60-80N/ mm2 |
Water absorption rate (23 ° C × 10 days) |
0.10-0.20 %by wt. | |
| Flexural strength | 100- 130N/ mm2 |
Water absorption rate (100 ° C × 60 minutes) |
0.08-0.15 %by wt. | |
| Compressive strength | 140- 190N/ mm2 | Surface resistivity | 1014 Ω | |
| Impact strength | 8- 16kJ/ m2 | Volume resistivity | 1015 Ω.cm | |
| Curing shrinkage | 0.8- 1.0% | Dielectric strength | 31 kv/mm | |
| Flame resistance (4mm) | HB level | Dielectric loss | 0.02 | |
| Thermal conductivity | 0.8-0.9W/mk |
|
Storage Storage of the components should be kept at 6-35℃ in tightly sealed and dry. Under these conditions, the shelf life should be correspond to the package labeled ( normally 12 months). After this date, the product may be re-analysis to confirm if it validate yet. Partial emptied containers should be closed tightly immediately after use. |
|
Package Epoxy resin 20kg/pail or 220kg/pail or 1200kg/pail, Hardener 20kg/pail or 220kg/pail or 1200kg/pail. |
|
First Aid Contamination of eyes by resin, hardener of casting mix should be treated immediately by flushing with clean,running water for 10 to 15minutes, a doctor should then be consulted. Material smeared or splashed on the skin should be dabbed off, and the contaminated area then washed and treated with a cleaning cream. A doctor should be on the event of severe imitation of burns. Contaminated clothing should be changed immediately. Anyone taken ill after inhaling vapors should be moved out of doorsimmediately,in all case of doubt call for medical assistance. |